Although all glass mosaic inherited characteristic points, due to the different production processes, so the difference between the cold spray hot melt mosaic mosaics and more obvious:

 

Cold spray crystal glass mosaic:

 

It is the first transparent plate glass mechanical or manual referral, cut to size or shape of the mosaic-like glass blocks, the furnace at a relatively low temperature specific heat melt the referral, the cutting edge side firing arc shape, the Artificial visually pick qualified products placed in a particular mold, to form printing machine in which the inner side of the spray paint of various colors or color between the coating, drying and then covered with a layer of white paint more rough by then After drying in the front or back of the stickers affixed to the network, from the finished product packaging.

 

 

Hot melt crystal glass mosaic:

 

First certain thickness (usually 4-8mm) finished transparent plate glass referral into a certain area and form lumps, and then in one side printed on the color of the glaze or glaze after repeated printed pattern, dried and then printed layer of white glaze (to prevent friction glaze is a glaze flaking and increase grain thickness), dried again, by mechanical or manual referral, cut to size, size, shape, mosaic pieces, by placed in the pipeline or artificial material sprinkled with silicic acid-ho on (increased hardness and rough glaze improves adhesion) of the same type of high-temperature ceramic quality plate, moving forward in the mix sintering furnace heat balance harmony glass open mediated side firing arc edge shape, the line after a furnace natural cooling or a special shelf placement cooling, cooling gradation workers visual screening method, the qualified products into certain specification mold or the back of the grid in front Stickers posted net, then drying the adhesive after a good package for the finished product.

 

Because of different processes, cold spray sprayand hot melt mosaic mosaic difference will be different:

 

1, The mosaic is the result of high temperature hot melt sintering, uniform color naturally.

 

2, Cold spray mosaic color is sprayed on the back, edge processing is not clean, use a period of time will be very easy to fade, there is that you can use a nail or something hard in the back of the two mosaics of scratch, you can see the heat melting mosaic differences, and recommend the use of hot melt mosaics.